Container: 0.5 kgTechnical data: Base: epoxy resin, aluminium-filled
Specific property: pasty
Colour after curing: aluminium
Mixing ratio by weight resin/hardener: 100:20
Viscosity of the mixture: 880,000 mPa·s
Consumption when 1.0 mm is applied: 1.60 kg/m²
Max. layer thickness per operation: 10 mm
Pot life at +20°C (+68°F) with 200 g batch: 60 min.
Can be subjected to mechanical loading after: 16 hours
Final hardness after: 24 hours
Average strength at +25°C (+77°F) according to DIN 53281-83/ASTM D 1002:
Compressive strength: 61 MPa
Bending strength: 37 MPa
Modulus of elasticity: 1500-2000 MPa
Shore D hardness (ATSM D 1706): 84
Shrinkage: 0.02%
Heat resistance: +60°CPasty, aluminium-filled, non-corrosive and antimagnetic
WEICON F is especially suitable for use on parts made of aluminium, aluminium alloy, magnesium and other light metals. WEICON F can be used for cost-effective repairs of all kinds, for filling cavities in light metal castings and for reconstructing parts. The epoxy resin system can be used in toolmaking, in model and mould making, and in many other areas of industry.